Publication

Abstract : Recent advances in coronary stents have all been distinctively focused towards directing re-endothelialization with minimal in-stent restenosis, potentially via alterations in surface topographical cues, for augmenting the efficacy of vascular implants. This perspective was proven by our group utilizing a simple and easily scalable nanosurface modification strategy on metallic stents devoid of any drugs or polymers. In the present work, we explore the impact of surface characteristics in modulating this cell response in-vitro and in-vivo, using titania coated cobalt-chromium (CC) stents, with and without nanotopography, in comparison to commercial controls. Interestingly, titania nanotopography facilitated a preferential cell response in-vitro as against the titania coated and bare CC surfaces, which can be attributed to surface topography, hydrophilicity, and roughness. This in turn altered the cellular adhesion, proliferation and focal contact formations of endothelial and smooth muscle cells. We also demonstrate that titania nanotexturing plays a pivotal role in fostering rapid re-endothelialization with minimal neointimal hyperplasia, leading to excellent in-vivo patency of CC stents post 8 weeks implantation in rabbit iliac arteries, in comparison to bare CC, nano-less titania coated CC, and commercial drug-eluting stents (CC DES), without administering antiplatelet agents. This exciting result for the drug and polymer-free titania nanotextured stents, in the absence of platelet therapy, reveals the possibility of proposing an alternative to clinical DES for coronary stenting.